Table 2 Mechanical properties obtained from the uniaxial tests of the MEO2MA elastomers prepared with different amounts of HPR-C as a cross-linker.
0.5 wt %
HPR-C
1.0 wt %
HPR-C
2.0 wt %
HPR-C
4.0 wt %
HPR-C
Young’s modulus E
(kPa)
125280349400
Extension at break λ
(mm/mm)
760620615481
U (kPa)70.8102.2138.3145.9
Γ (J/m2)415.9703.11019.11320.2